DLP Materials
ROBUST MATERIALS & STRONG, END-USE PARTS
Develop materials, products, and processes – then scale to large quantities. All on the same production-ready platform. Check out the pre-qualified materials below.
HEAT RESISTANT
TOUGH
GENERAL PURPOSE
ELASTOMERS
MEDICAL
DENTAL
Smarter Production
It takes an ecosystem to transform an industry. Stratasys works with leading chemical companies to co-develop innovative photopolymers to unlock end-use applications in 3D printing. Choose from a wide range of single component, commercial-grade materials, developed on and validated for Origin machines.
Heat Resistant
LOCTITE 3D 3955 FST
First photopolymer that passes vertical burn and aerospace FST standards.
Colors: Black
Ultimate Tensile Strength: 67 MPa
Elongation at Break: 2%
Tensile Modulus: 3556 MPa
HDT: >300°C
LOCTITE 3D IND403
High modulus tough resin for high temperature resistance.
Colors: Black
Ultimate Tensile Strength: 72 MPa
Elongation at Break: 10%
Tensile Modulus: 2572 MPa
HDT: 80° C
LOCTITE 3D IND3380 ESD
The smooth surface and high chemical resistance make it an ideal choice for jigs & fixtures and electronic manufacturing.
Colors: Black
Tensile Elongation at Break: 2%
Flexural Modulus: 1250-1350 MPa
Flexural Strength: 40-50 MPa
HDT: 190° C
P3 Deflect 190 ESD
High strength, HDT ESD material.
Colors: Black
Ultimate Tensile Strength: 40 – 50 MPa
Elongation at Break: 1 – 2%
Tensile Modulus: 3200 – 3400 MPa
HDT: 190°C
Somos PerFORM HW
High stiffness, heat resistant material designed for applications such as tools for injection molding.
Colors: Off-white
Tensile Elongation at Break: 1.4%
Flexural Modulus: 8,700 MPa
Flexural Strength: 60 MPa
HDT: 160° C
Ultracur3D RG 3280
Ceramic-filled photopolymer with exceptional stiffness, high heat resistance, and dimensional stability under pressure.
Colors: White
Ultimate Tensile Strength: 87 MPa
Elongation at Break: 1.3%
Tensile Modulus: 10600 MPa
HDT: 284°C
Tough
LOCTITE 3D 3172
Tough and high impact for fixtures and tooling.
Colors: Cyan, Gray
Ultimate Tensile Strength: 39 MPa
Elongation at Break: 105%
Tensile Modulus: 1494 MPa
HDT: 51° C
LOCTITE 3D 3843
High-impact, semi-flexible resin suitable for a broad range of applications.
Colors: Black, White, Clear
Ultimate Tensile Strength: 53 MPa
Elongation at Break: 43%
Tensile Modulus: 1806 MPa
HDT: 60° C
LOCTITE 3D IND405
Smooth surface finish and good impact resistance, ideal for mechanical guides, fluid ducts, and microfluidic devices.
Colors: Clear
Ultimate Tensile Strength: 52 MPa
Elongation at Break: 127%
Tensile Modulus: 1378 MPa
HDT: 53° C
Stratasys Dura56
Durable, impact resistant photopolymer for functional applications where aesthetics and robustness are critical.
Colors: Black
Ultimate Tensile Strength: 44 MPa
Elongation at Break: 78%
Tensile Modulus: 1595 MPa
HDT: 52° C
General Purpose
Ultracur3D ST45
Reactive urethane polymer for high-performance functional parts.
Colors: Black, Clear
Ultimate Tensile Strength: 53 MPa
Elongation at Break: 21%
Tensile Modulus: 2000 MPa
HDT: 63° C
Somos WeatherX 100
Environmentally durable material designed for end-use parts.
Colors: Black
Ultimate Tensile Strength: 60 ± 0.3 MPa
Elongation at Break: 26% ± 6.0
Tensile Modulus: 2128 ± 154 MPa
HDT: 67° C
Elastomers
EL150
Reactive urethane photopolymer for prototyping.
Colors: Clear
Ultimate Tensile Strength: 6 MPa
Elongation at Break: 150%
Tensile Modulus: 25 MPa
LOCTITE 3D IND402
High rebound elastomer with high resilience, ideal for lattice structures.
Colors: Black
Ultimate Tensile Strength: 5.5 MPa
Elongation at Break: 230%
Tensile Modulus: 42 MPa
P3 Stretch IND475
Resilient, low shore hardness elastomer with good tear strength.
Colors: Black
Ultimate Tensile Strength: 2.4 MPa
Elongation at Break: 122%
Tensile Modulus: 2.5 MPa
P3 Stretch 80
General-purpose elastomer for flexible prototypes.
Colors: Black
Ultimate Tensile Strength: 11 ± 2.4 MPa
Elongation at Break: 117% ± 17.4
Tensile Modulus: 54 ± 4.5 MPa
Medical
LOCTITE 3D MED 412
Flexible material ideal for gaskets, elastomeric lattice foam replacements, and anatomical models.
Colors: Clear, White
Ultimate Tensile Strength: 37 MPa
Elongation at Break: 110%
Tensile Modulus: 1305 MPa
HDT: 39° C
LOCTITE 3D MED 413
Biocompatible material designed for general medical purposes.
Colors: Clear
Ultimate Tensile Strength: 46 MPa
Elongation at Break: 51%
Tensile Modulus: 1673 MPa
HDT: 68° C
Dental
DM100
Dental model resin with optional combination of strength, impact resistance, and dimensional stability.
Tensile Strength: 70 MPa
Elongation at Break: 5%
Tensile Modulus: 2000 MPa
HDT @ 0.45 MPa: 54°C
DM200
Low viscosity material tailored to produce dental models quickly with high accuracy and quality.
Tensile Strength: 40 MPa
Elongation at Break: 10-20%
Tensile Modulus: 1600-2300 MPa
HDT @ 0.45 MPa: 45°C
FotoDent
Light-curing resin for the production of denture bases.
Flexural Strength: >80 MPa
Flexural Modulus: >2000 MPa
Hardness: >80 Shore D
KeyCast
This low shrinkage material controls thermal expansion to yield porous-free and accurate castings.
Flexural Strength: 15 MPa
Elongation at Break: 16%
Flexural Modulus: 340 MPa
Shrinkage: <2%
Burnout: <0.05%
KeyDenture Try In
Photopolymer resin intended for short-term trial dentures, evaluation of fit, occlusion, esthetics, and phonetics.
Flexural Strength: 56-68 MPa
Elongation at Break: 30-43%
Flexural Modulus: 1500-1750 MPa
Biocompatibility: Pass
KeyGuide
Strong, biocompatible resin best for fabricating transparent and stable surgical guides.
Flexural Strength: 105 MPa
Elongation at Break: 6.3%
Flexural Modulus: 2400 MPa
Biocompatibility: Pass
KeyMask
Flexible yet firm gingival mask that simulates the look and feel of gum tissue.
Tensile Strength: 2 MPa
Elongation at Break: 41%
Tensile Modulus: 4.6 MPa
KeyOrtho IBT
This material accurately sets brackets with the flexibility and non-stick formula needed for easy release.
Tensile Strength: 8-10.5 MPa
Elongation at Break: >130%
Tensile Modulus: 15.5-31 MPa
Orthodontic Adhesive Release: Pass
KeySplint Hard
Dental material made for rigid dental splints, retainers, and post-trauma tooth immobilization.
Flexural Strength: 60-65 MPa
Elongation at Break: 9%
Flexural Modulus: 1510-1600 MPa
Biocompatibility: Pass
KeySplint Soft
Strong and flexible resin ideal for printing splints, night guards, and bleaching trays.
Tensile Strength: 52 MPa
Elongation at Break: 110%
Tensile Modulus: 1790 MPa
Biocompatibility: Pass
KeyTray
Strong, biocompatible resin designed to create customized, individual impression trays quickly and with precision.
Flexural Strength: 84.7 MPa
Elongation at Break: 26.4%
Flexural Modulus: 1913 MPa
Shore D Hardness: 86.5 D