Origin One Materials
ROBUST MATERIALS & STRONG, END-USE PARTS
Develop materials, products, and processes – then scale to large quantities. All on the same production-ready platform: Origin One. Check out the pre-qualified materials below.
HEAT RESISTANT
TOUGH
GENERAL PURPOSE
ELASTOMERS
MEDICAL
DENTAL
Smarter Production
It takes an ecosystem to transform an industry. Stratasys works with leading chemical companies to co-develop innovative photopolymers to unlock end-use applications in 3D printing. Choose from a wide range of single component, commercial-grade materials, developed on and validated for Origin One.
Heat Resistant
Loctite 3D 3955 FST
First photopolymer that passes vertical burn and aerospace FST standards.
Colors: Black
Ultimate Tensile Strength: 67 MPa
Elongation at Break: 2%
Tensile Modulus: 3556 MPa
HDT: >300°C
Loctite 3D IND403
High modulus tough resin for high temperature resistance.
Colors: Black
Ultimate Tensile Strength: 72 MPa
Elongation at Break: 10%
Tensile Modulus: 2572 MPa
HDT: 80° C
P3 Deflect 120
High strength and heat resistant photopolymer that is easy to process.
Colors: Black
Ultimate Tensile Strength: 89 MPa
Elongation at Break: 6%
Tensile Modulus: 3200 MPa
HDT: 120°C
Tough
Loctite 3D 3172
Tough and high impact for fixtures and tooling.
Colors: Cyan, Gray
Ultimate Tensile Strength: 39 MPa
Elongation at Break: 105%
Tensile Modulus: 1494 MPa
HDT: 51° C
Loctite 3D 3843
High-impact, semi-flexible resin suitable for a broad range of applications.
Colors: Black, White, Clear
Ultimate Tensile Strength: 53 MPa
Elongation at Break: 43%
Tensile Modulus: 1806 MPa
HDT: 60° C
Loctite 3D IND405
Smooth surface finish and good impact resistance, ideal for mechanical guides, fluid ducts, and microfluidic devices.
Colors: Clear
Ultimate Tensile Strength: 52 MPa
Elongation at Break: 127%
Tensile Modulus: 1378 MPa
HDT: 53° C
Stratasys Dura56
Durable, impact resistant photopolymer for functional applications where aesthetics and robustness are critical.
Colors: Black
Ultimate Tensile Strength: 44 MPa
Elongation at Break: 78%
Tensile Modulus: 1595 MPa
HDT: 52° C
General Purpose
Somos QuickGen 500
Fast-printing, flexible resin for general and functional prototypes.
Colors: Clear
Ultimate Tensile Strength: 20 MPa
Elongation at Break: 42%
Tensile Modulus: 465 MPa
HDT: 62° C
Ultracur3D ST45
Reactive urethane polymer for high-performance functional parts.
Colors: Black, Clear
Ultimate Tensile Strength: 53 MPa
Elongation at Break: 21%
Tensile Modulus: 2000 MPa
HDT: 63° C
Elastomers
EL150
Reactive urethane photopolymer for prototyping.
Colors: Clear
Ultimate Tensile Strength: 6 MPa
Elongation at Break: 150%
Tensile Modulus: 25 MPa
Loctite 3D IND402
High rebound elastomer with high resilience, ideal for lattice structures.
Colors: Black
Ultimate Tensile Strength: 5.5 MPa
Elongation at Break: 230%
Tensile Modulus: 42 MPa
P3 Stretch IND475
Resilient, low shore hardness elastomer with good tear strength.
Colors: Black
Ultimate Tensile Strength: 2.4 MPa
Elongation at Break: 122%
Tensile Modulus: 2.5 MPa
Medical
Loctite 3D MED 412
Flexible material ideal for gaskets, elastomeric lattice foam replacements, and anatomical models.
Colors: Clear, White
Ultimate Tensile Strength: 37 MPa
Elongation at Break: 110%
Tensile Modulus: 1305 MPa
HDT: 39° C
Loctite 3D MED 413
Biocompatible material designed for general medical purposes.
Colors: Clear, White
Ultimate Tensile Strength: 46 MPa
Elongation at Break: 51%
Tensile Modulus: 1673 MPa
HDT: 68° C
Dental
KeyGuide
Light-curing resin for the fabrication of biocompatible dental surgical guides.
Colors: Clear
Flexural Strength: 106 MPa
Flexural Modulus: 2400 MPa
Elongation at Break: 6.3%
KeySplint Soft
Light-curing resin for flexible, biocompatible dental devices.
Colors: Light Violet, Translucent
Flexural Strength: 44-47 MPa
Flexural Modulus: 1,100-1,400 MPa
Elongation at Break: >110%
Origin DM100
High-strength resin used for accurate dental models.
Colors: Beige
Ultimate Tensile Strength: 70 MPa
Elongation at Break: 5%
Tensile Modulus: 2000 MPa
HDT: 54°C
Origin DM200
High-accuracy material with faster speed times meant for all dental model applications.
Colors: Beige
Ultimate Tensile Strength: >40 MPa
Elongation at Break: 10-20%
Tensile Modulus: 1600-2300 MPa
HDT: 45°C
Origin One Materials
ROBUST MATERIALS & STRONG, END-USE PARTS
Develop materials, products, and processes – then scale to large quantities. All on the same production-ready platform: Origin One. Check out the pre-qualified materials below.
Smarter Production
It takes an ecosystem to transform an industry. Stratasys works with leading chemical companies to co-develop innovative photopolymers to unlock end-use applications in 3D printing. Choose from a wide range of single component, commercial-grade materials, developed on and validated for Origin One.
Heat Resistant
3955
First photopolymer that passes vertical burn and aerospace FST standards.
Colors: Black
Ultimate Tensile Strength: 67 MPa
Elongation At Break: 2%
Tensile Modulus: 3556 MPa
HDT: >300° C
403
High modulus tough resin for high temperature resistance.
Colors: Black
Ultimate Tensile Strength: 72 MPa
Elongation At Break: 10%
Tensile Modulus: 2572 MPa
HDT: 80° C
Tough
3843
High-impact, semi-flexible resin suitable for a broad range of applications.
Colors: Black, White, Clear
Ultimate Tensile Strength: 53 MPa
Elongation At Break: 43%
Tensile Modulus: 1806 MPa
HDT: 60° C
Dura56
Durable, impact resistant photopolymer for functional applications where aesthetics and robustness are critical.
Colors: Black
Ultimate Tensile Strength: 44 MPa
Elongation At Break: 78%
Tensile Modulus: 1595 MPa
HDT: 52° C
3172
Tough and high impact for fixtures and tooling.
Colors: Cyan, Gray
Ultimate Tensile Strength: 39 MPa
Elongation At Break: 105%
Tensile Modulus: 1494 MPa
HDT: 51° C
IND405
Smooth surface finish and good impact resistance, ideal for mechanical guides, fluid ducts, and microfluidic devices.
Colors: Clear
Ultimate Tensile Strength: 52 MPa
Elongation At Break: 127%
Tensile Modulus: 1378 MPa
HDT: 53° C
General Purpose
ST45
Reactive urethane polymer for high-performance functional parts.
Colors: Black, Clear
Ultimate Tensile Strength: 53 MPa
Elongation At Break: 21%
Tensile Modulus: 2000 MPa
HDT: 63° C
QG 500
Fast-printing, flexible resin for general and functional prototypes.
Colors: Clear
Ultimate Tensile Strength: 20 MPa
Elongation At Break: 42%
Tensile Modulus: 465 MPa
HDT: 62° C
Elastomers
402
High rebound elastomer with high resilience, ideal for lattice structures.
Colors: Black
Ultimate Tensile Strength: 5.5 MPa
Elongation At Break: 230%
Tensile Modulus: 42 MPa
EL150
Reactive urethane photopolymer for prototyping.
Colors: Clear
Ultimate Tensile Strength: 6 MPa
Elongation At Break: 150%
Tensile Modulus: 25 MPa
Medical
MED412
Flexible material ideal for gaskets, elastomeric lattice foam replacements, and anatomical models.
Ultimate Tensile Strength: 37 MPa
Elongation At Break: 110%
Tensile Modulus: 1305 MPa
HDT: 39° C
MED413
Biocompatible material designed for general medical purposes.
Ultimate Tensile Strength: 46 MPa
Elongation At Break: 51%
Tensile Modulus: 1673 MPa
HDT: 68° C
Origin One Materials
ROBUST MATERIALS & STRONG, END-USE PARTS
Develop materials, products, and processes – then scale to large quantities. All on the same production-ready platform: Origin One. Check out the pre-qualified materials below.
Smarter Production
It takes an ecosystem to transform an industry. Stratasys works with leading chemical companies to co-develop innovative photopolymers to unlock end-use applications in 3D printing. Choose from a wide range of single component, commercial-grade materials, developed on and validated for Origin One.
Heat Resistant
3955
First photopolymer that passes vertical burn and aerospace FST standards.
Colors: Black
Ultimate Tensile Strength: 67 MPa
Elongation At Break: 2%
Tensile Modulus: 3556 MPa
HDT: >300° C
403
High modulus tough resin for high temperature resistance.
Colors: Black
Ultimate Tensile Strength: 72 MPa
Elongation At Break: 10%
Tensile Modulus: 2572 MPa
HDT: 80° C
Tough
3843
High-impact, semi-flexible resin suitable for a broad range of applications.
Colors: Black, White, Clear
Ultimate Tensile Strength: 53 MPa
Elongation At Break: 43%
Tensile Modulus: 1806 MPa
HDT: 60° C
Dura56
Durable, impact resistant photopolymer for functional applications where aesthetics and robustness are critical.
Colors: Black
Ultimate Tensile Strength: 44 MPa
Elongation At Break: 78%
Tensile Modulus: 1595 MPa
HDT: 52° C
3172
Tough and high impact for fixtures and tooling.
Colors: Cyan, Gray
Ultimate Tensile Strength: 39 MPa
Elongation At Break: 105%
Tensile Modulus: 1494 MPa
HDT: 51° C
IND405
Smooth surface finish and good impact resistance, ideal for mechanical guides, fluid ducts, and microfluidic devices.
Colors: Clear
Ultimate Tensile Strength: 52 MPa
Elongation At Break: 127%
Tensile Modulus: 1378 MPa
HDT: 53° C
General Purpose
ST45
Reactive urethane polymer for high-performance functional parts.
Colors: Black, Clear
Ultimate Tensile Strength: 53 MPa
Elongation At Break: 21%
Tensile Modulus: 2000 MPa
HDT: 63° C
QG 500
Fast-printing, flexible resin for general and functional prototypes.
Colors: Clear
Ultimate Tensile Strength: 20 MPa
Elongation At Break: 42%
Tensile Modulus: 465 MPa
HDT: 62° C
Elastomers
402
High rebound elastomer with high resilience, ideal for lattice structures.
Colors: Black
Ultimate Tensile Strength: 5.5 MPa
Elongation At Break: 230%
Tensile Modulus: 42 MPa
EL150
Reactive urethane photopolymer for prototyping.
Colors: Clear
Ultimate Tensile Strength: 6 MPa
Elongation At Break: 150%
Tensile Modulus: 25 MPa
Medical
MED412
Flexible material ideal for gaskets, elastomeric lattice foam replacements, and anatomical models.
Ultimate Tensile Strength: 37 MPa
Elongation At Break: 110%
Tensile Modulus: 1305 MPa
HDT: 39° C
MED413
Biocompatible material designed for general medical purposes.
Ultimate Tensile Strength: 46 MPa
Elongation At Break: 51%
Tensile Modulus: 1673 MPa
HDT: 68° C